PR-1100 / PR-1130 / PR-1120 / PR-1125
PR-1100
| Properties | Unit | Value | Test Method |
|---|---|---|---|
| Gel Time | Min | 10 ± 2 | ASTM D2471 |
| Max Cure Time | Min | 24 ± 2 | ASTM D2471 |
| Exothermic Peak | ℃ | 180 ± 10 | ASTM D2471 |
| Acid Value | mg KOH/gr | 35 ± 2 | ASTM D1639 |
| Solid Content | % | 65 ± 2 | ASTM D1259 |
| Viscosity (25 ℃) | Ford Cup | 60 ± 10 | ISO 2555 |
| Density | g/ml | 1.13 ± 0.02 | ISO 1675 |
| Shelf Life | Months | 3 |
0.1% Co 6% and 2 % MEKP to 100 g resin at 25 °C
| Properties | Unit | Value | Test Method |
|---|---|---|---|
| Tensile Strength | Mpa | 35 ± 5 | ISO 527-2/1A/2 |
| Flexural Strength | Mpa | 65 ± 10 | ISO 178 |
| HDT | ℃ | 48 ± 5 | ISO 75-2/Method 1e |
| Hardness | Barcol | 30 ± 5 | ASTM D2583 | Water Absorption | % | 0.30 ± 0.02 | ISO 62/Method 3 |
For Fully Cured resin : 0.25% Co 6% and 2 % MEKP to 100 g resin at 25 °C
1.24hrs at 25 °C,4 hrs at 90 °C
2.Curing Schedule : 24 hrs at 25 °C,4 hrs at 90 °C ,3 hrs at 120 °C
PR-1130
| Properties | Unit | Value | Test Method |
|---|---|---|---|
| Gel Time | Min | 10 ± 2 | ASTM D2471 |
| Max Cure Time | Min | 20 ± 2 | ASTM D2471 |
| Exothermic Peak | ℃ | 170 ± 10 | ASTM D2471 |
| Acid Value | mg KOH/gr | ± 2 | ASTM D1639 |
| Solid Content | % | 65 ± 2 | ASTM D1259 |
| Viscosity (25 ℃) | Ford Cup | 60 ± 10 | ISO 2555 |
| Density | g/ml | 1.13 ± 0.02 | ISO 1675 |
| Shelf Life | Months | 3 |
0.1% Co 6% and 2 % MEKP to 100 g resin at 25 °C
| Properties | Unit | Value | Test Method |
|---|---|---|---|
| Tensile Strength | Mpa | 40 ± 5 | ISO 527-2/1A/2 |
| Flexural Strength | Mpa | 70 ± 10 | ISO 178 |
| HDT | ℃ | 50 ± 5 | ISO 75-2/Method 1e |
| Hardness | Barcol | 30 ± 5 | ASTM D2583 |
| Water Absorption | % | 0.28 ± 0.02 | ISO 62/Method 3 |
For Fully Cured resin : 0.25% Co 6% and 2 % MEKP to 100 g resin at 25 °C
1.24hrs at 25 °C,4 hrs at 90 °C
2.Curing Schedule : 24 hrs at 25 °C,4 hrs at 90 °C ,3 hrs at 120 °C
PR-1120
| Properties | Unit | Value | Test Method |
|---|---|---|---|
| Gel Time | Min | 10 ± 2 | ASTM D2471 |
| Max Cure Time | Min | 18 ± 2 | ASTM D2471 |
| Exothermic Peak | ℃ | 180 ± 10 | ASTM D2471 |
| Acid Value | mg KOH/gr | 26 ± 2 | ASTM D1639 |
| Solid Content | % | 65 ± 2 | ASTM D1259 |
| Viscosity (25 ℃) | Ford Cup | 60 ± 10 | ISO 2555 |
| Density | g/ml | 1.13 ± 0.02 | ISO 1675 |
| Shelf Life | Months | 3 |
0.1% Co 6% and 2 % MEKP to 100 g resin at 25 °C
| Properties | Unit | Value | Test Method |
|---|---|---|---|
| Tensile Strength | Mpa | 58 ± 5 | ISO 527-2/1A/2 |
| Flexural Strength | Mpa | 72 ± 10 | ISO 178 |
| HDT | ℃ | 50 ± 5 | ISO 75-2/Method 1e |
| Hardness | Barcol | 20 ± 5 | ASTM D2583 |
| Water Absorption % | 0.30 ± 0.02 | ISO 62/Method 3 |
For Fully Cured resin : 0.25% Co 6% and 2 % MEKP to 100 g resin at 25 °C
1.24hrs at 25 °C, 4 hrs at 90 °C
2.Curing Schedule : 24 hrs at 25 °C,4 hrs at 90 °C ,3 hrs at 120 °C
PR-1125
| Properties | Unit | Value | Test Method |
|---|---|---|---|
| Gel Time | Min | 9 ± 2 | ASTM D2471 |
| Max Cure Time | Min | 17 ± 2 | ASTM D2471 |
| Exothermic Peak | ℃ | 170 ± 10 | ASTM D2471 |
| Acid Value | mg KOH/gr | 24 ± 2 | ASTM D1639 |
| Solid Content | % | 65 ± 2 | ASTM D1259 |
| Viscosity (25 ℃) | Ford Cup | 45 ± 10 | ISO 2555 |
| Density | g/ml | 1.13 ± 0.02 | ISO 1675 |
| Shelf Life | Months | 3 |
0.1% Co 6% and 2 % MEKP to 100 g resin at 25 °C
| Properties | Unit | Value | Test Method |
|---|---|---|---|
| Tensile Strength | Mpa | 50 ± 5 | ISO 527-2/1A/2 |
| Flexural Strength | Mpa | 75 ± 10 | ISO 178 |
| HDT | ℃ | 54 ± 5 | ISO 75-2/Method 1e |
| Hardness | Barcol | 35 ± 5 | ASTM D2583 |
| Water Absorption | % | 0.27 ± 0.02 | ISO 62/Method 3 |
For Fully Cured resin : 0.25% Co 6% and 2 % MEKP to 100 g resin at 25 °C
1.24hrs at 25 °C,4 hrs at 90 °C
2.Curing Schedule : 24 hrs at 25 °C,4 hrs at 90 °C ,3 hrs at 120 °C
Persia Resin sculpture-grade polyester resins are engineered to meet the functional requirements of unsaturated polyester systems used in decorative casting and detailed molded components. Key characteristics such as controlled viscosity, moderate exothermic reaction, predictable gel time, and acceptable volumetric shrinkage place these resins within the standard performance range expected for sculpture and ornamental resin applications.
Compared to premium casting systems specifically developed for ultra-low shrinkage, extended pot life, or optical clarity, Persia Resin sculpture resins prioritize dimensional consistency, mold-filling capability, and controlled curing behavior over specialized visual or preservation-focused features. This formulation approach supports reliable replication of fine surface details while maintaining manageable curing temperatures in medium-thickness castings.
Overall, these resins align with common market benchmarks for decorative polyester casting materials, offering a technically balanced solution for sculpture, architectural ornamentation, and mold-based decorative production where repeatability and process control are critical.