Pultrusion

PR-1400 / PR-1420 / PR-2000

PR-1400

PROPERTIES OF LIQUID FORM
Properties	Unit	Value	Test Method
Gel Time	Min	10 ± 2	ASTM D2471
Max Cure Time	Min	20 ± 2	ASTM D2471
Exothermic Peak	℃	170 ± 5	ASTM D2471
Acid Value	mg KOH/gr	18 ± 2	ASTM 1639
Solid Content	%	65 ± 2	ASTM D1259
Viscosity (25 ℃)	Ford Cup	50 ± 10	ISO 2555
Density	g/ml	1.13 ± 0.02	ISO 1675
Shelf Life	Months	3

0.1% Co 6% and 2 % MEKP to 100 g resin at 25 °C

MECHANICAL PROPERTIES OF CURED RESIN
Properties	Unit	Value	Test Method
Tensile Strength	Mpa	50 ± 5	ISO 527-2/1A/2
Flexural Strength	Mpa	75 ± 10	ISO 178
HDT	℃	55 ± 5	ISO 75-2/Method 1e
Hardness	Barcol	30 ± 5	ASTM D2583
Water Absorption	%	0.18 ± 0.02	ISO 62/Method 3

For Fully Cured resin : 0.25% Co 6% and 2 % MEKP to 100 g resin at 25 °C

1. 24 hrs at 25 °C,4 hrs at 90 °C

2. Curing Schedule : 24 hrs at 25 °C,4 hrs at 90 °C ,3 hrs at 120 °C

PROPERTIES OF LIQUID FORM
Properties	Unit	Value	Test Method
Gel Time	Min	10 ± 2	ASTM D2471
Max Cure Time	Min	20 ± 2	ASTM D2471
Exothermic Peak	℃	188 ± 5	ASTM D2471
Acid Value	mg KOH/gr	18 ± 2	ASTM 1639
Solid Content	%	65 ± 2	ASTM D1259
Viscosity (25 ℃)	Ford Cup	90 ± 10	ISO 2555
Density	g/ml	1.13 ± 0.02	ISO 1675
Shelf Life	Months	3

0.1% Co 6% and 2 % MEKP to 100 g resin at 25 °C

MECHANICAL PROPERTIES OF CURED RESIN
Properties	Unit	Value	Test Method
Tensile Strength	Mpa	42 ± 5	ISO 527-2/1A/2
Flexural Strength	Mpa	100 ± 10	ISO 178
HDT	℃	65 ± 5	ISO 75-2/Method 1e
Hardness	Barcol	30 ± 5	ASTM D2583
Water Absorption	%	0.18 ± 0.02	ISO 62/Method 3

For Fully Cured resin : 0.25% Co 6% and 2 % MEKP to 100 g resin at 25 °C

1. 24 hrs at 25 °C,4 hrs at 90 °C

2. Curing Schedule : 24 hrs at 25 °C,4 hrs at 90 °C ,3 hrs at 120 °C

PROPERTIES OF LIQUID FORM
Properties	Unit	Value	Test Method
Gel Time	Min	6 ± 2	ASTM D2471
Max Cure Time	Min	12 ± 2	ASTM D2471
Exothermic Peak	℃	210 ± 10	ASTM D2471
Acid Value	mg KOH/gr	20 ± 2	ASTM 1639
Solid Content	%	62 ± 2	ASTM D1259
Viscosity (25 ℃)	Ford Cup	170 ± 10	ISO 2555
Density	g/ml	1.11 ± 0.02	ISO 1675
Shelf Life	Months	3

0.2% Co 6% and 2 % MEKP to 100 g resin at 25 °C

MECHANICAL PROPERTIES OF CURED RESIN
Properties	Unit	Value	Test Method
Tensile Strength	Mpa	24 ± 5	ISO 527-2/1A/2
Flexural Strength	Mpa	90 ± 10	ISO 178
HDT	℃	95 ± 5	ISO 75-2/Method 1e
Hardness	Barcol	40 ± 5	ASTM D2583
Water Absorption	%	0.29 ± 0.02	ISO 62/Method 3

For Fully Cured resin : 0.5% Co 6% and 2 % MEKP to 100 g resin at 25 °C

1. 24 hrs at 25 °C,4 hrs at 90 °C

2. Curing Schedule : 24 hrs at 25 °C,4 hrs at 90 °C ,3 hrs at 120 °C